Two Component CIBA
Epoxy Adhesives |
 |
|
|
|
LIQUID TWO COMPONENT
EPOXY ADHESIVE
A transparent low viscosity adhesive |
|
|
|
|
|
Product |
Araldite AY 103/ |
Hardener HY 991 |
|
Mix Ration by wt/by vol |
100:40/ |
100:/50 |
|
Viscosity, Components,cP |
1,600 |
23,000 |
|
Mixed Viscosity cP |
3500 |
|
|
Specific Gravity Components |
1.15 |
0.93 |
|
Pot Life Min @ 77F |
90 |
|
|
Handling Strength hrs @ 77F |
12 |
|
|
Mnimum Cure Time
Hrs @ 77F
MIn @ 140F
Min @ 212F |
24
120
15
|
|
|
Lap Shear Strength
psi @ 77F
psi @ 180F |
2,300
700
|
|
|
Tg F/C |
181/83 |
|
|
Elongation % |
9 |
|
|
Ultimate Tensile Strength psi |
6,200 |
|
|
Hardness Shore D |
84 |
|
|
Maximum Service Temp F/C |
140/60 |
|
|
|
|
|
MEDIUM VISCOSITY TWO
COMPONENT EPOXY ADHESIVE
Transparent adhesive with high reactivity
above 160F/70C.
Bonds fiberglass, plastics and wood. |
|
|
|
|
Product |
TDR 1100/11 Resin |
TDR 1100-11 Hardener |
|
Mix Ration by wt/by vol |
100:42 |
100:50 |
|
Viscosity, Components,cP |
16,500 |
38,000 |
|
Mixed Viscosity cP |
13,000 |
|
|
Specific Gravity Components |
1.16 |
0.99 |
|
Pot Life Min @ 77F |
95 |
|
|
Handling Strength hrs @ 77F |
8 |
|
|
Mnimum Cure Time
Hrs @ 77F
MIn @ 140F
Min @ 212F |
24
60
15
|
|
|
Lap Shear Strength
psi @ 77F
psi @ 180F |
4,100
3,200
|
|
|
Tg F/C |
185/85 |
|
|
Elongation % |
5 |
|
|
Ultimate Tensile Strength psi |
9,000 |
|
|
Hardness Shore D |
85 |
|
|
Maximum Service Temp F/C |
195/90 |
|
|
|
|
|
HIGH VISCOSITY TWO COMPONENT
EPOXY ADHESIVE
Fast setting adhesive that cures at temperatures as low as
41F/5C. For bonding and repairing small parts. |
|
|
|
|
Product |
Fastweld 10 Resin |
Fastweld 10 Hardener |
|
Mix Ration by wt/by vol |
100:100 |
100:100 |
|
Viscosity, Components,cP |
260,000 |
160,000 |
|
Mixed Viscosity cP |
250,000 |
|
|
Specific Gravity Components |
1.48 |
1.44 |
|
Pot Life Min @ 77F |
4 |
|
|
Handling Strength hrs @ 77F |
10 min |
|
|
Mnimum Cure Time
Hrs @ 77F
MIn @ 140F
Min @ 212F |
4
NR
NR
|
|
|
Lap Shear Strength
psi @ 77F
psi @ 180F |
2,840
220
|
|
|
Tg F/C |
127/53 |
|
|
Elongation % |
5 |
|
|
Ultimate Tensile Strength psi |
3,850 |
|
|
Hardness Shore D |
85 |
|
|
Maximum Service Temp F/C |
140/60 |
|
|
|
|
|
PASTE TWO COMPONENT EPOXY
ADHESIVES
Araldite/Hardener 1253 Mahogany-colored
paste that is easy to sand and hand-carve. For repair and bonding of wood
products.
Araldite/Hardener 1258 Gap-filling,
aluminum-filled paste that is easy to machine. For general-purpose
bonding and repair.. |
|
|
|
|
Product |
Araldite AV 1253/ |
Hardener HV 1253 |
Araldite AV 1258/ |
Hardener HV 1258 |
|
Mix Ration by wt/by vol |
100:82/ |
100:/100 |
100:/100 |
100:/100 |
|
Viscosity, Components,cP |
Paste |
Paste |
Paste |
Paste |
|
Mixed Viscosity cP |
Paste |
Paste |
Paste |
Paste |
|
Specific Gravity Components |
0.82 |
0.64 |
1.53 |
1.56 |
|
Pot Life Min @ 77F |
20 |
|
23 |
|
|
Handling Strength hrs @ 77F |
3.5 |
|
3.5 |
|
|
Mnimum Cure Time
Hrs @ 77F
MIn @ 140F
Min @ 212F |
6
30
10
|
|
6
30
10
|
|
|
Lap Shear Strength
psi @ 77F
psi @ 180F |
1,990
140
|
|
2,840
330
|
|
|
Tg F/C |
146/63 |
|
166/74 |
|
|
Elongation % |
11 |
|
2 |
|
|
Ultimate Tensile Strength psi |
2,250 |
|
5,600 |
|
|
Hardness Shore D |
73 |
|
89 |
|
|
Maximum Service Temp F/C |
120/50 |
|
140/60 |
|
|
|
|
Glu